316L Polished Stainless Steel Sheet For Various Sizes

Basic Information
Place of Origin: CHINA
Brand Name: TISCO,LISCO,ZPSS,JISCO
Certification: SGS,TUV
Model Number: 316L
Minimum Order Quantity: 2 tons
Price: Negotiable
Packaging Details: cold rolled waterproof paper and steel strip reinforcement,one package about 2 tons,Load in 20' or 40' GP
Delivery Time: 3-5 working days
Payment Terms: L/C, T/T
Supply Ability: 800tons per month
Detail Information
Thickness: 0.3-6.0mm Finish: Polished
Carbon: Low Carbon Technique: Cold Rolled
Width: 1200 1000 1219mm As Your Request Length: 2400 2440 2000 3000mm As Your Request
Shape: Sheet/plate/coil/pipe/bar Edge: Slit,Mill
Other Grade: 304 304L 201 430 321 309s 310s 2205 904L Ect
High Light:

ss sheet metal

,

stainless steel slab


Product Description

Cold rolled 316L Polished Stainless Steel Sheet for Various Sizes

 

316L stainless Steel adds Mo (2-3%), so it has excellent corrosion resistance and high temperature strength; SUS316L carbon content is lower than SUS316, therefore, the resistance to inter-granular corrosion resistance is better than SUS316: high temperature creep strength is high. It can be used in harsh conditions.good strain hardening and non-magnetic.
1) cold-rolled product appearance, good gloss, beautiful;
2) the addition of Mo, corrosion resistance, especially resistance to pitting corrosion;
3) excellent high temperature strength
4) Excellent hardening (after processing weakly magnetic)
5) solid solution state non-magnetic;
6) relative to 304 stainless steel, it has higher prices.(10Ni)

                                

316L Stainless Steel Composition
Table 1. Composition ranges for 316L stainless steels.          
Grade   C Mn Si P
316L Min - - - -
Max 0.03 2 0.75 0.045
316L Stainless SteelMechanical Properties
Table 2. Mechanical properties of 316L stainless steels.          
Grade Tensile Str (MPa) min Yield Str 0.2% Proof (MPa) min Elong (% in 50 mm) min Hardness
Rockwell B (HR B) max Brinell (HB) max
316L 485 170 40 95 217
 

 

316L stainless steel Sheet
Standard Grade Chemical Composition % Technique Yied strength/Mpa Tensile strength/Mpa Elongation % Hardness
GB 00Cr17Ni14M02

C≤0.030,Mn≤2.00,

Si≤1.00,P≤0.045,

S≤0.030,

Cr 16.0~18.0,Ni 10.0~14.0,Mo 2.00~3.00

cold /hot rolled ≥177 ≥485 ≥40 HV≤200
USA 316L
JIS SUS316L
German 1.4404

 

Welding
Excellent weldability by all standard fusion and resistance methods, both with and without filler metals. Heavy welded sections in Grade 316 require post-weld annealing for maximum corrosion resistance. This is not required for 316L.
316L stainless steel is not generally weldable using oxyacetylene welding methods.

Machining
316L stainless steel tends to work harden if machined too quickly. For this reason low speeds and constant feed rates are recommended.
316L stainless steel is also easier to machine compared to 316 stainless steel due its lower carbon content.

316L Polished Stainless Steel Sheet For Various Sizes 0

Hot and Cold Working
316L stainless steel can be hot worked using most common hot working techniques. Optimal hot working temperatures should be in the range 1150-1260°C, and certainly should not be less than 930°C. Post work annealing should be carried out to induce maximum corrosion resistance.
Most common cold working operations such as shearing, drawing and stamping can be performed on 316L stainless steel. Post work annealing should be carried out to remove internal stresses.

Hardening and Work Hardening
316L stainless steel does not harden in response to heat treatments. It can be hardened by cold working, which can also result in increased strength.

 

316L Polished Stainless Steel Sheet For Various Sizes 1

 

 

 

SINO INOX would appreciate to get your esteemed enquires and look forward to the pleasure receiving your valuable response.

Thanking you and assuring our best services at all times.For more check on our web.

http://www.sinossteel.com  

E-mail : sale@sinosinox.com

Contact Details
Lily

Phone Number : +8618626358302

WhatsApp : +8618626358302